Surface coated ZnO powder as flame retardant for wood: A short communication

Abstract

In the present study, the ability of a coating of zinc oxide (ZnO) powder to improve the fire-safety of wood exposed to radiative heat flux was examined, focusing on the ignition time of the wood. To test ZnO's efficiency on the wood sub- strate, two different amounts of ZnO (0.5 and 1 g ZnO per dm2 ) were applied to the wood surface and exposed to ra- diative heat from a cone calorimeter wherein a pristine piece of wood with no ZnO treatment was taken as control. The experiments were conducted at three different irradiation levels i.e., 20, 35, and 50 kWm?2 . The results showed that applying ZnO on the surface of the wood significantly increased the ignition time (TTI). For the three different heat fluxes, using 0.5 g ZnO per dm2 coating on the wood surface increased the TTI by 26–33 %. Furthermore, the applica- tion of 1 g of ZnO per dm2 generated a TTI increment of 37–40 %. All three irradiation levels showed similar trends in TTI. The micrographs taken before and after combustion showed no significant disparity in the morphology of ZnO. The agglomerated ZnO particles on the wood surface remained intact after combustion. This study demonstrates a fac- ile method of using ZnO to delay the ignition of wood. This could potentially impart fire-safety to wooden structures/ façades in wildland-urban interfaces and elsewhere by reducing flame spread.